ASTM A320 Grade B8T (321 Stainless)
321 stainless bolting certified to A320 — titanium stabilized against sensitization, impact exempt above −325 °F, for cold service on welded stainless equipment.
What A320 B8T is.
Everything in this grade is the same steel as ASTM A193 B8T: identical 321 chemistry, the same heat treatment classes and the same room-temperature strength table. What A320 adds is the framework for cold service — impact testing rules, the requirement that nuts come from the matching austenitic A194 grade, and certification to a specification that piping and vessel codes call out for sub-zero design temperatures.
B8T is the titanium-stabilized counterpart of B8C and is used the same way: on cold-service equipment that is welded or thermally cycled and must not sensitize. A320 places B8T with the −325 °F exemption group rather than the −425 °F group, so the deepest cryogenic duty is usually ordered as B8 or B8C, or as B8T with an agreed impact test.
Chemical composition.
| Element | Symbol | Min % | Max % |
|---|---|---|---|
| Carbon | C | — | 0.08 |
| Manganese | Mn | — | 2.00 |
| Phosphorus | P | — | 0.045 |
| Sulfur | S | — | 0.030 |
| Silicon | Si | — | 1.00 |
| Chromium | Cr | 17.0 | 19.0 |
| Nickel | Ni | 9.0 | 12.0 |
| Titanium | Ti | 5 × (C+N) | 0.70 |
| Nitrogen | N | — | 0.10 |
Values per ASTM A320/A320M-26, Tables 1 and 3 (verified against the specification). Confirm the edition called out on your purchase order with our estimating team.
Mechanical properties.
| Nominal diameter (in.) | Tensile strength, min (ksi) | Yield strength 0.2% offset, min (ksi) | Elongation in 2 in., min (%) | Reduction of area, min (%) | Hardness, max |
|---|---|---|---|---|---|
| Class 1 — all diameters | 75 | 30 | 30 | 50 | 223 HBW / 96 HRB |
| Class 1A (B8TA) — all diameters | 75 | 30 | 30 | 50 | 192 HBW / 90 HRB |
| Class 2 — ¾ and under | 125 | 100 | 12 | 35 | 321 HBW / 35 HRC |
| Class 2 — over ¾ to 1 | 115 | 80 | 15 | 35 | 321 HBW / 35 HRC |
| Class 2 — over 1 to 1¼ | 105 | 65 | 20 | 35 | 321 HBW / 35 HRC |
| Class 2 — over 1¼ to 1½ | 100 | 50 | 28 | 45 | 321 HBW / 35 HRC |
Values per ASTM A320/A320M-26, Tables 1 and 3 (verified against the specification). Confirm the edition called out on your purchase order with our estimating team. Class 1 sizes ¾ in. and smaller may be 241 HBW / 100 HRB. Class 2 is limited to 1½ in. Strain-hardened austenitic steel may not show uniform properties through the section, particularly over ¾ in. diameter.
| Grade and class | Impact test exempt above | Below that temperature |
|---|---|---|
| B8, B8C, B8P, B8LN — Class 1 and 1A | −425 °F (−254 °C) | Impact tested to agreed criteria |
| B8M, B8T, B8F, B8MLN — Class 1 and 1A | −325 °F (−198 °C) | Impact tested to agreed criteria |
| All austenitic grades — Class 2 | −325 °F (−198 °C) | Impact tested to agreed criteria |
| Any grade ½ in. and smaller | Exempt at all temperatures | Unless S1 is specified |
Per ASTM A320/A320M-26 (verified against the specification). When impact tests are required for austenitic grades, the test temperature and acceptance criteria are agreed between purchaser and supplier; Supplementary Requirement S1 may be ordered.
Specifications that apply.
How A320 B8T ships from Houston.
- Full-thread studs and stud bolts
- Double-end and tap-end studs
- Hex and heavy hex bolts
- Socket head cap screws
- Threaded rod (cut and rolled thread)
- Machined components from certified bar
A320 B8T fasteners we make.
Every item is manufactured to your drawing or standard in A320 B8T, imperial or metric, with an EN 10204 3.1 certificate.
What is ASTM A320 B8T?
A320 B8T is 321 austenitic stainless bolting certified for low-temperature service. Titanium at five times the carbon-plus-nitrogen content ties up carbon as titanium carbide, so 321 resists intergranular attack after welding or after service in the 800 to 1500 °F range. Its low-temperature toughness is that of the 18-8 family. Under A320 it is available in Class 1, Class 1A (B8TA) and strain-hardened Class 2 (B8TSH), with impact exemption above −325 °F.
Impact testing under A320
- Class 1 and 1A material of this grade is exempt from impact testing above −325 °F. Below that, the test temperature and acceptance values are agreed between purchaser and supplier, or ordered under Supplementary Requirement S1.
- Class 2 (strain hardened) austenitic bolting is exempt above −325 °F.
- Bolting ½ in. and smaller is exempt at all temperatures unless S1 is specified.
- Nuts follow 10.2: matching A194 austenitic grades, with the same exemption temperatures.
Why order to A320 instead of A193?
The mechanical numbers are the same, so the choice comes down to what the design code and the purchaser's specification ask for. ASME B31.3 and Section VIII list SA-320 for bolting below the A193 minimum temperatures, and an A320 certificate carries the impact-test statement, or the exemption under 6.2.1.1, that a low-temperature package needs. Ordering A320 also brings in 10.2, which requires austenitic A194 nuts of the matching grade and states when those nuts must be impact tested. Dual-certified A193/A320 bolting is available on request when a stock item must serve both.
Testing, certification and marking
- Tensile and hardness tested per lot on the finished product
- Grade symbol B8T (B8TSH for Class 2) and manufacturer's identification on every piece
- EN 10204 3.1 material test report with heat number and chemistry; 3.2 witness available
- Impact test results, or the 6.2.1.1 exemption, stated on the certificate
- Nuts from A194 Grade 8T, impact tested when the service temperature requires it
ASTM A193 Grade B8T Class 1 (321 Stainless)
321 stainless bolting stabilised with titanium — the match for 321 piping and vessels in hot, cyclic and welded service.
ASTM A320 / ASME SA-320ASTM A320 Grade B8C (347 Stainless)
347 stainless bolting certified to A320 — niobium stabilized against sensitization, impact exempt above −425 °F, for cold service that also sees weld heat or thermal cycling.
ASTM A320 / ASME SA-320ASTM A320 Grade B8 Class 1 (304 Stainless)
304 stainless bolting certified to the low-temperature specification — the same 75 ksi solution-treated material as A193 B8, with A320 impact rules and matching A194 Grade 8 nuts.